UHP 350mm Graphite Electrodes Amin'ny Electrolysis Ho an'ny Fandrendrehana vy
Parameter ara-teknika
| fikirana | anjara | Unit | UHP 350mm(14") data |
| Nominal savaivony | Electrode | mm (inch) | 350(14) |
| Max savaivony | mm | 358 | |
| Savaivony Min | mm | 352 | |
| Nominal Length | mm | 1600/1800 | |
| Max Length | mm | 1700/1900 | |
| Halavany Min | mm | 1500/1700 | |
| Max ankehitriny Density | KA/cm2 | 20-30 | |
| Fahaizana mitondra amin'izao fotoana izao | A | 20000-30000 | |
| Fanoherana manokana | Electrode | μΩm | 4.8-5.8 |
| nonon'ny | 3.4-4.0 | ||
| Hery flexural | Electrode | Mpa | ≥12.0 |
| nonon'ny | ≥22.0 | ||
| Ny Modulus Young | Electrode | Gpa | ≤13.0 |
| nonon'ny | ≤18.0 | ||
| Bulk Density | Electrode | g/cm3 | 1.68-1.72 |
| nonon'ny | 1.78-1.84 | ||
| CTE | Electrode | ×10-6/℃ | ≤1.2 |
| nonon'ny | ≤1.0 | ||
| Votoatin'ny lavenona | Electrode | % | ≤0.2 |
| nonon'ny | ≤0.2 |
FANAMARIHANA: Ny fepetra manokana momba ny refy dia azo atolotra.
Naoty vokatra
Graphite electrode naoty dia mizara ho hery ara-dalàna graphite electrode (RP), hery avo graphite electrode (HP), ultra hery avo graphite electrode (UHP).
Fampiharana indrindra ho an'ny lafaoro Arc elektrika amin'ny fanaovana vy
Graphite electrodes ho an'ny vy fanaovana kaonty ho an'ny 70-80% ny totalin'ny graphite electrodes fampiharana. Amin'ny alàlan'ny fampitaovana herinaratra avo lenta sy zotra mankany amin'ny electrode graphite, ny arc elektrika dia hipoitra eo anelanelan'ny tendron'ny electrode sy ny koba metaly izay hamokatra hafanana be hanalefaka ny koba. Ny dingan'ny fandrendrehana dia handevona ny electrode graphite, ary tsy maintsy soloina tsy tapaka.
Ny UHP graphite electrode dia matetika ampiasaina amin'ny indostrian'ny vy mandritra ny famokarana vy elektrika arc (EAF). Ny dingan'ny EAF dia ny fandoroana vy sisa mba hamokarana vy vaovao. Ny electrode graphite UHP dia ampiasaina amin'ny famoronana arc elektrika, izay manafana ny vy vy mankany amin'ny teboka miempo. Ity dingana ity dia mahomby sy tsy misy vidiny, satria mamela ny famokarana haingana sy be dia be ny vy.
Fizarana Fijerena sy Fijerena drafitra momba ny lafaoro Arc elektrika
Izahay no mpanamboatra manana tsipika famokarana feno sy ekipa matihanina.
30% TT mialoha ho fandoavam-bola, Ny 70% mandanjalanja TT alohan'ny fanaterana.
Vokatra mifandraika
-
Fampiasana Electrode Graphite ho an'ny fanadiovana korundum ...
Tabilao ara-teknika 1: Parametera ara-teknika ho an'ny savaivony kely grafita elektrôda savaivony ampahany fanoherana ny tanjaky ny Modulus tanora CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥5.0 ≤9.0 ≤ -1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 Nip...
-
Soderberg Carbon Electrode Mametaka ho an'ny Ferroallo...
Toetra ara-teknika voaisy tombo-kase Electrode Past Standard Electrode paste GF01 GF02 GF03 GF04 GF05 Volatile Flux(%) 12.0-15.5 12.0-15.5 9.5-13.5 11.5-15.5 11.5-15.5 11.5-15.5 Compressive 22.0 21.0 20.0 Resisitivity(uΩm) 65 75 80 85 90 Volom Density(g/cm3) 1.38 1.38 1.38 1.38 1.38 Elongation(%) 5-20 5-20 5-40 15-40 15-40 % ...
-
High Density kely savaivony lafaoro Graphite El ...
Tabilao ara-teknika 1: Parametera ara-teknika ho an'ny savaivony kely grafita elektrôda savaivony ampahany fanoherana ny tanjaky ny Modulus tanora CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥5.0 ≤9.0 ≤ -1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 Nip...
-
Hery tsy tapaka Electrode Graphite savaivony kely...
Tabilao ara-teknika 1: Parametera ara-teknika ho an'ny savaivony kely grafita elektrôda savaivony ampahany fanoherana ny tanjaky ny Modulus tanora CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥5.0 ≤9.0 ≤ -1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64...
-
Lafaoro Graphite Electrode kely savaivony 75mm ...
Tabilao ara-teknika 1: Parametera ara-teknika ho an'ny savaivony kely grafita elektrôda savaivony ampahany fanoherana ny tanjaky ny Modulus tanora CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥5.0 ≤9.0 ≤ -1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 Nip...
-
Low Sulfur FC 93% Carburizer Carbon Raiser Iro...
Graphite Petroleum Coke (GPC) Fikirakirana Karbonina (FC) Volatile (VM) Sulphur(S) Ash Nitrogen(N) Hydrogène(H) Hamandoana ≥98% ≤1% 0≤0.05% ≤1% ≤0.03% ≤0.01% ≤0.5% ≥98.5% ≤0,8% ≤0,05% ≤0,7% ≤0,03% ≤0,01% ≤0,5% ≥99% ≤0,5% ≤0,03% ≤0,5% ≤0,03% ≤0,03% ≤0,03% ≤ 0-0.50mm, 5-1mm, 1-3mm, 0-5mm, 1-5mm, 0-10mm, 5-10mm, 5-10mm, 10-15mm na amin'ny safidy mpanjifa Fonosana: 1. Waterproof ...