Mpanamboatra elektrôda grafita sinoa 450mm savaivony RP HP UHP Elektroda grafita
Parameter ara-teknika
| fikirana | anjara | Unit | RP 450mm(18") Data |
| Nominal savaivony | Electrode | mm (inch) | 450 |
| Max savaivony | mm | 460 | |
| Savaivony Min | mm | 454 | |
| Nominal Length | mm | 1800/2400 | |
| Max Length | mm | 1900/2500 | |
| Halavany Min | mm | 1700/2300 | |
| Max ankehitriny Density | KA/cm2 | 13-17 | |
| Fahaizana mitondra amin'izao fotoana izao | A | 22000-27000 | |
| Fanoherana manokana | Electrode | μΩm | 7.5-8.5 |
| nonon'ny | 5.8-6.5 | ||
| Hery flexural | Electrode | Mpa | ≥8.5 |
| nonon'ny | ≥16.0 | ||
| Ny Modulus Young | Electrode | Gpa | ≤9.3 |
| nonon'ny | ≤13.0 | ||
| Bulk Density | Electrode | g/cm3 | 1.55-1.64 |
| nonon'ny | ≥1.74 | ||
| CTE | Electrode | ×10-6/℃ | ≤2.4 |
| nonon'ny | ≤2.0 | ||
| Votoatin'ny lavenona | Electrode | % | ≤0.3 |
| nonon'ny | ≤0.3 |
FANAMARIHANA: Ny fepetra manokana momba ny refy dia azo atolotra.
Surface Quality Ruler
- Ny lesoka na ny lavaka dia tsy tokony hihoatra ny ampahany roa amin'ny elektrônika grafita, ary ny lesoka na ny haben'ny lavaka dia tsy avela hihoatra ny angon-drakitra ao amin'ny tabilao etsy ambany.
- Tsy misy transverse triatra eo amin'ny electrode surface.Ho an'ny longitudinal triatra, ny halavany dia tokony ho tsy mihoatra ny 5% ny graphite electrode circumference, ny sakany dia tokony ho ao anatin'ny 0.3-1.0mm range.Longitudinal crack data ambany 0.3mm angona dia tokony ho tsinontsinona.
- Ny sakan'ny faritra marokoroko (mainty) eo amin'ny grafofaonina electrode ambonin'ny dia tokony ho tsy latsaky ny 1/10 ny graphite electrode circumference, ary ny halavan'ny faritra marokoroko (mainty) faritra mihoatra ny 1/3 ny graphite electrode halavan'ny dia tsy. avela.
Angon-drakitra tsy fahampiana amin'ny elektrôda grafit
| Nominal savaivony | Data tsy fahampiana (mm) | ||
| mm | mirefy | Savaivony (mm) | Halany (mm) |
| 300-400 | 12-16 | 20–40 | 5–10 |
| 450-700 | 18-24 | 30–50 | 10–15 |
Vokatra mifandraika
-
Electrodes Graphite dia mampiasa vy amin'ny Nippl ...
Paramètre ara-teknika Paramètre Fizarana RP 500mm(20") Data Nominal Diameter Electrode mm(inch) 500 Max Diameter mm 511 Min Diameter mm 505 Nominal Halavan'ny mm 1800/2400 Max Halavan'ny mm 1900/2500 Min Halavan'ny mm 1700/2300 Haavony ankehitriny KA /cm2 13-16 Ankehitriny Fahaizana mitondra A 25000-32000 Electrode fanoherana manokana μΩm 7.5-8.5 Nipple 5.8-6.5 Flexur ...
-
High Purity Sic Silicon Carbide Crucible Graphi...
Silicon Carbide Crucible Performance Parameter Data Parameter Data SiC ≥85% Cold Crushing Strength ≥100MPa SiO₂ ≤10% Hita Porosity ≤%18 Fe₂O₃ <1% Temperature Resistance ≥1700°C Bulk Density ≥1700°C Bulk Density. tsara conductivity thermal --- Manana thermal tsara izy io ...
-
Fampiasana Electrode Graphite ho an'ny fanadiovana korundum ...
Tabilao ara-teknika 1: Parametera ara-teknika ho an'ny savaivony kely grafita elektrôda savaivony ampahany fanoherana ny tanjaky ny Modulus tanora CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥5.0 ≤9.0 ≤ -1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 Nip...
-
Kely savaivony graphite Electrodes rod ho an'ny Elec ...
Tabilao ara-teknika 1: Parametera ara-teknika ho an'ny savaivony kely grafita elektrôda savaivony ampahany fanoherana ny tanjaky ny Modulus tanora CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥5.0 ≤9.0 ≤ -1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 Nip...
-
UHP 700mm Graphite Electrode lehibe savaivony Gra ...
Parametera ara-teknika Paramètre Fizarana UHP 700mm(28") Data Nominal Diameter Electrode mm(inch) 700 Max Diameter mm 714 Min Diameter mm 710 Nominal Halavan'ny mm 2200/2700 Max Halavan'ny mm 2300/2800 Min Halavan'ny mm 2100/2600 Min Halavany mm 2100/2600 Min Haavony /cm2 18-24 Ankehitriny Fahaizana mitondra A 73000-96000 Electrode fanoherana manokana μΩm 4.5-5.4 Nipple 3.0-3.6 Flexu ...
-
Silicon Graphite Crucible Ho an'ny Metal Melting Cla...
Parameter ara-teknika ho an'ny Clay Graphite Crucible SIC C Modulus of Rupture Temperature Resistance Bulk Density Hita mibaribary Porosity ≥ 40% ≥ 35% ≥10Mpa 1790 ℃ ≥2.2 G / CM3 ≤15% Fanamarihana: Afaka manitsy ny votoatin'ny akora manta tsirairay isika araka ny takian'ny mpanjifa. Famaritana Ny grafita ampiasaina amin'ireo koveta ireo dia matetika atao...